Evaluation of the Durability of Concrete made with Black Slag from Electric Arc Furnace
Keywords:
black slag, concrete, durability, properties
Abstract
Steel companies generate a large volume of black slag in the production of steel, which represents an environmental problem that increases over time, a solution being to give this waste added value in the manufacture of concrete, either as aggregate or as supplementary cementitious material. The objective of this research was to evaluate the durability properties of concrete made with black slag as coarse aggregate. Some durability properties of concrete were measured: resistivity, ultrasonic pulse velocity, chloride ion penetration and depth of penetration of pressurized water., using the methodology of replacing 100% of the natural coarse aggregate with crushed black slag, and comparing it with concrete patron. The results showed that the manufactured concrete presented durability properties slightly lower than those that used natural aggregate, in particular, there was evidence of a probability of corrosion of the steel reinforcement bars. But this should not constitute a cause for rejection, but rather an element to be taken into account when using it, such as mass concrete or concrete reinforced with polymer bars, and creates guidelines to continue researching with others for smaller replacement rates
Downloads
Download data is not yet available.
References
Aguilar, P. (2024). Evaluación de los impactos ambientales en la cantera Taparachi generados por la explotación de materiales empleados en la construcción. Revista Multidisciplinar Ciencia Latina, 8(2), 1307-1326.
Andrea, Y., Vera, E. (2021). Compressive strength of concrete made with electric arc furnace slag and recycled ground glass as replacement of coarse and fine aggregate. Revista Ingeniería de Construcción, 36(3), 342-360.
Asociación Española de Normalización, UNE-EN 12390-8 (2020). “Ensayos de hormigón endurecido. Parte 8: Profundidad de penetración de agua bajo presión”, Madrid, España.
ASTM International, ASTM 595/595M (2021). “Standard Specification for Blended Hydraulic Cements”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States.
ASTM International, ASTM C 597 (2022). “Standard Test Method for Ultrasonic Pulse Velocity Through Concrete”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
ASTM International, ASTM C 1202 (2012). “Standard Test Method for Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
ASTM International, ASTM C 1760 (2021). “Standard Test Method for Bulk Electrical Conductivity of Hardened Concrete”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
Benítez, P., Rocha, E., Rodrigues, M. (2020). Estrategias para la inspección óptima de estructuras de hormigón armado sujetas a corrosión. Revista Ciencia Tecnología e Innovación, 2(2), 46-58.
Camacaro, A., Picón, L., Sánchez, M., T., de Rincón, O., Millano, V. (2023). Evaluación de los daños por corrosión de una estructura de concreto armado expuesta a un ambiente costero industrial. Revista Técnica de la Facultad de Ingeniería de la Universidad del Zulia, 40, e234615.
Castañeda, A., Corvo, F., Pech, I., Valdés, C., Marrero, R., Ángel, M. (2021). Atmospheric corrosion in an oil refinery located on a tropical island under new pollution situation. Journal of Materials Engineering and Performance, 30(32).
Castañeda, A., Valdés, C., Viña, J., Verdecia, U., Corvo, F., Marrero, R. (2021). Comparación de la penetración de iones cloruro en los pilotes de hormigón armado de la Terminal de Cruceros en la bahía de La Habana, Cuba. XVI Congreso Latinoamericano de Patología de la Construcción y XVIII de Control de la Calidad de la Construcción (CONPAT-2021). Río de Janeiro, Associação Brasileira de Patologia das Construções, ID-455, Sección 7C – Control.
Cedeño de Sánchez, A., Hernández, C., Ortiz de Vergara, F., Villar, J. (2022). Acción del microambiente sobre el concreto reforzado. Revista Prisma Tecnológico, 13(1), 10-16.
Chiné, B., Jiménez, R., Cuevas, R. (2024). Modelación computacional de la corrosión del refuerzo metálico de un concreto carbonatado. Revista Tecnología en Marcha, 37(1), 51-64.
Chiriboga, C. (2022). Influencia de la corrosión en varillas de acero de refuerzo y sus efectos en la resistencia estructural de edificaciones. Journal Scientific MQRInvestigar, 6(4), 396-419.
Costa, M., Valões, D., Nascimento, C., Lima, E., Silva, G., Silva, T., Santos, T. (2022). Analysis of concrete characteristics with the replacement of natural fine aggregate by industrial solid waste. Revista ALCONPAT, 12(3), 328-343.
De la Roz, I., Puig, R. (2021). Mathematical model to predict the compressive strength of concrete in 28 days. Revista Cubana de Ingeniería, 12(1), 58-66.
Dhanabal, P., Sushmitha, K. (2022). Effect of iron ore tailing and glass powder on concrete properties. Revista Ingeniería de Construcción, 37(1), 47-57.
Fogliatti, F., Carrasco, M., Beltramini, L., Defagot, C. (2023). Effect of past and fine aggregate content on pervious concrete. Revista Tecnología y Ciencia. 21(46), 18-40.
Freitas, M., Meira, G. (2023). Transport capacity of chloride ions in concretes with mineral additions used in Brazil. Revista ALCONPAT. 13(1), 61-79.
Guerra, J., Castañeda, A., Corvo, F., Howland, J., Rodríguez, J. (2019). Atmospheric corrosión of low carbón steel in a coastal zone of Ecuador: Anomalous behavior of chloride deposition versus distance from the sea. Materials and Corrosion, 70(3), 444-460.
Guerra, J., Puig, R., Castañeda, A., Baque, B. (2023). Estado del arte sobre durabilidad de las estructuras de hormigón armado en perfiles costeros. Revista INGENIAR: Ingeniería, Tecnología e Investigación, 6(11), 2-20.
Llanos, J., Sota, E., Huaricallo, Y., Romero, Y. (2023). Analysis of concrete f'c = 175 kg/cm2, 210 kg/cm2, 245 kg/cm2 and 280 kg/cm2 of low permeability, subjected to high water pressures. 21st LACCEI International Multi-Conference for Engineering, Education and Technology. Buenos Aires, Latin American and Caribbean Conference for Engineering and Technology, Session 38B T4-P2, LACCEI2023.1.1.557.
Lorenzi, A., Chies, J., Adamatti, D., Silva, L. (2017). Evaluación de la capacidad de detección de fallas en el concreto a través del ensayo ultrasónico. Revista ALCONPAT, 7(3), 286-301.
Mendoza, J. M., Díaz, J. H. (2023). Circular economy in the Latin American cement and concrete industry: a sustainable solution of design, durability, materials, and processes. Revista ALCONPAT, 13(3), 328-348.
Oficina Nacional de Normalización, NC 231 (2002). “Determinación, interpretación y aplicación de la velocidad del pulso ultrasónico en el hormigón”, La Habana, Cuba.
Oficina Nacional de Normalización, NC 248 (2005). “Hormigón endurecido – Determinación de la profundidad de penetración de agua bajo presión”, La Habana, Cuba.
Oficina Nacional de Normalización, NC 412 (2005). “Guía para la preparación, mezclado, transporte y vertido del hormigón, La Habana, Cuba.
Oficina Nacional de Normalización, NC 1340 (2020). “Cemento – Especificaciones”, La Habana, Cuba.
Oficina Nacional de Normalización, NC ISO 1920-2 (2010). “Ensayos al hormigón – Parte 2: Propiedades del hormigón fresco”, La Habana, Cuba.
Oficina Nacional de Normalización, NC-ISO 1920-3 (2010). “Ensayos al hormigón – Parte 3: Elaboración y curado de probetas para ensayos, La Habana, Cuba.
Ossorio, A., Lorenzo, R. (2014). Predicción de la vida útil de las estructuras de hormigón armado mediante un modelo de difusión de iones cloruro. Revista de la Facultad de Ingeniería de la Universidad de Antioquía, 72, 161-172.
Pérez, Y., Vera, E., Ochoa, R. (2021). Morphological, chemical, and mineralogical characterization of concrete mixtures produced by electric arc furnace slag. Journal of Physics: Conference Series, 2046(1), 012035.
Rashad, M. (2022). Behavuir of slag aggregate in mortar and concrete – A comprehensive overview. Journal of Building Engineering, 53, 104536.
Rea, A. R. (2023). Daño ambiental y economía circular en la explotación de los recursos naturales no renovables. Revista FIGEMPA: Investigación y Desarrollo, 16(2), 93-103.
Rojas, M., Otálvaro, I., Pérez, J., Mauricio, H., Ambriz, C. (2021). Uso de las escorias de horno de arco eléctrico (EHAE) en la construcción - estado del arte. Revista UIS Ingenierías, 20(2), 53-64.
Socarrás, Y. C., González, L., Álvarez, E., González, M., Roca, E. (2020). Evaluación de la calidad del hormigón en edificaciones construidas con el sistema prefabricado Gran Panel. Revista Tecnología Química, 40(2), 264-277.
Sohail, M., Laurens, S., Deby, F., Balayssac, J., Nuaimi, N. (2021). Electrochemical corrosion parameters for active and passive reinforcing steel in carbonated and sound concrete. Materials and Corrosion, 72(12), 1854-1871.
Villao, R. (2021). Actualidad de las técnicas de análisis de corrosión en estructuras de concreto reforzado. Journal of Engineering Sciences, 3(8), 1-10.
Zhang, Y., Su, R. (2019). Concrete cover delamination model for non-uniform corrosion of reinforcements. Construction and Building Materials, 223(2), 329-340.
Andrea, Y., Vera, E. (2021). Compressive strength of concrete made with electric arc furnace slag and recycled ground glass as replacement of coarse and fine aggregate. Revista Ingeniería de Construcción, 36(3), 342-360.
Asociación Española de Normalización, UNE-EN 12390-8 (2020). “Ensayos de hormigón endurecido. Parte 8: Profundidad de penetración de agua bajo presión”, Madrid, España.
ASTM International, ASTM 595/595M (2021). “Standard Specification for Blended Hydraulic Cements”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States.
ASTM International, ASTM C 597 (2022). “Standard Test Method for Ultrasonic Pulse Velocity Through Concrete”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
ASTM International, ASTM C 1202 (2012). “Standard Test Method for Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
ASTM International, ASTM C 1760 (2021). “Standard Test Method for Bulk Electrical Conductivity of Hardened Concrete”, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
Benítez, P., Rocha, E., Rodrigues, M. (2020). Estrategias para la inspección óptima de estructuras de hormigón armado sujetas a corrosión. Revista Ciencia Tecnología e Innovación, 2(2), 46-58.
Camacaro, A., Picón, L., Sánchez, M., T., de Rincón, O., Millano, V. (2023). Evaluación de los daños por corrosión de una estructura de concreto armado expuesta a un ambiente costero industrial. Revista Técnica de la Facultad de Ingeniería de la Universidad del Zulia, 40, e234615.
Castañeda, A., Corvo, F., Pech, I., Valdés, C., Marrero, R., Ángel, M. (2021). Atmospheric corrosion in an oil refinery located on a tropical island under new pollution situation. Journal of Materials Engineering and Performance, 30(32).
Castañeda, A., Valdés, C., Viña, J., Verdecia, U., Corvo, F., Marrero, R. (2021). Comparación de la penetración de iones cloruro en los pilotes de hormigón armado de la Terminal de Cruceros en la bahía de La Habana, Cuba. XVI Congreso Latinoamericano de Patología de la Construcción y XVIII de Control de la Calidad de la Construcción (CONPAT-2021). Río de Janeiro, Associação Brasileira de Patologia das Construções, ID-455, Sección 7C – Control.
Cedeño de Sánchez, A., Hernández, C., Ortiz de Vergara, F., Villar, J. (2022). Acción del microambiente sobre el concreto reforzado. Revista Prisma Tecnológico, 13(1), 10-16.
Chiné, B., Jiménez, R., Cuevas, R. (2024). Modelación computacional de la corrosión del refuerzo metálico de un concreto carbonatado. Revista Tecnología en Marcha, 37(1), 51-64.
Chiriboga, C. (2022). Influencia de la corrosión en varillas de acero de refuerzo y sus efectos en la resistencia estructural de edificaciones. Journal Scientific MQRInvestigar, 6(4), 396-419.
Costa, M., Valões, D., Nascimento, C., Lima, E., Silva, G., Silva, T., Santos, T. (2022). Analysis of concrete characteristics with the replacement of natural fine aggregate by industrial solid waste. Revista ALCONPAT, 12(3), 328-343.
De la Roz, I., Puig, R. (2021). Mathematical model to predict the compressive strength of concrete in 28 days. Revista Cubana de Ingeniería, 12(1), 58-66.
Dhanabal, P., Sushmitha, K. (2022). Effect of iron ore tailing and glass powder on concrete properties. Revista Ingeniería de Construcción, 37(1), 47-57.
Fogliatti, F., Carrasco, M., Beltramini, L., Defagot, C. (2023). Effect of past and fine aggregate content on pervious concrete. Revista Tecnología y Ciencia. 21(46), 18-40.
Freitas, M., Meira, G. (2023). Transport capacity of chloride ions in concretes with mineral additions used in Brazil. Revista ALCONPAT. 13(1), 61-79.
Guerra, J., Castañeda, A., Corvo, F., Howland, J., Rodríguez, J. (2019). Atmospheric corrosión of low carbón steel in a coastal zone of Ecuador: Anomalous behavior of chloride deposition versus distance from the sea. Materials and Corrosion, 70(3), 444-460.
Guerra, J., Puig, R., Castañeda, A., Baque, B. (2023). Estado del arte sobre durabilidad de las estructuras de hormigón armado en perfiles costeros. Revista INGENIAR: Ingeniería, Tecnología e Investigación, 6(11), 2-20.
Llanos, J., Sota, E., Huaricallo, Y., Romero, Y. (2023). Analysis of concrete f'c = 175 kg/cm2, 210 kg/cm2, 245 kg/cm2 and 280 kg/cm2 of low permeability, subjected to high water pressures. 21st LACCEI International Multi-Conference for Engineering, Education and Technology. Buenos Aires, Latin American and Caribbean Conference for Engineering and Technology, Session 38B T4-P2, LACCEI2023.1.1.557.
Lorenzi, A., Chies, J., Adamatti, D., Silva, L. (2017). Evaluación de la capacidad de detección de fallas en el concreto a través del ensayo ultrasónico. Revista ALCONPAT, 7(3), 286-301.
Mendoza, J. M., Díaz, J. H. (2023). Circular economy in the Latin American cement and concrete industry: a sustainable solution of design, durability, materials, and processes. Revista ALCONPAT, 13(3), 328-348.
Oficina Nacional de Normalización, NC 231 (2002). “Determinación, interpretación y aplicación de la velocidad del pulso ultrasónico en el hormigón”, La Habana, Cuba.
Oficina Nacional de Normalización, NC 248 (2005). “Hormigón endurecido – Determinación de la profundidad de penetración de agua bajo presión”, La Habana, Cuba.
Oficina Nacional de Normalización, NC 412 (2005). “Guía para la preparación, mezclado, transporte y vertido del hormigón, La Habana, Cuba.
Oficina Nacional de Normalización, NC 1340 (2020). “Cemento – Especificaciones”, La Habana, Cuba.
Oficina Nacional de Normalización, NC ISO 1920-2 (2010). “Ensayos al hormigón – Parte 2: Propiedades del hormigón fresco”, La Habana, Cuba.
Oficina Nacional de Normalización, NC-ISO 1920-3 (2010). “Ensayos al hormigón – Parte 3: Elaboración y curado de probetas para ensayos, La Habana, Cuba.
Ossorio, A., Lorenzo, R. (2014). Predicción de la vida útil de las estructuras de hormigón armado mediante un modelo de difusión de iones cloruro. Revista de la Facultad de Ingeniería de la Universidad de Antioquía, 72, 161-172.
Pérez, Y., Vera, E., Ochoa, R. (2021). Morphological, chemical, and mineralogical characterization of concrete mixtures produced by electric arc furnace slag. Journal of Physics: Conference Series, 2046(1), 012035.
Rashad, M. (2022). Behavuir of slag aggregate in mortar and concrete – A comprehensive overview. Journal of Building Engineering, 53, 104536.
Rea, A. R. (2023). Daño ambiental y economía circular en la explotación de los recursos naturales no renovables. Revista FIGEMPA: Investigación y Desarrollo, 16(2), 93-103.
Rojas, M., Otálvaro, I., Pérez, J., Mauricio, H., Ambriz, C. (2021). Uso de las escorias de horno de arco eléctrico (EHAE) en la construcción - estado del arte. Revista UIS Ingenierías, 20(2), 53-64.
Socarrás, Y. C., González, L., Álvarez, E., González, M., Roca, E. (2020). Evaluación de la calidad del hormigón en edificaciones construidas con el sistema prefabricado Gran Panel. Revista Tecnología Química, 40(2), 264-277.
Sohail, M., Laurens, S., Deby, F., Balayssac, J., Nuaimi, N. (2021). Electrochemical corrosion parameters for active and passive reinforcing steel in carbonated and sound concrete. Materials and Corrosion, 72(12), 1854-1871.
Villao, R. (2021). Actualidad de las técnicas de análisis de corrosión en estructuras de concreto reforzado. Journal of Engineering Sciences, 3(8), 1-10.
Zhang, Y., Su, R. (2019). Concrete cover delamination model for non-uniform corrosion of reinforcements. Construction and Building Materials, 223(2), 329-340.
Published
2025-02-07
How to Cite
Bayle Yong, J., Alemán Carmenate, G. and Puig Martínez, R. A. (2025) “Evaluation of the Durability of Concrete made with Black Slag from Electric Arc Furnace”, Revista Técnica de la Facultad de Ingeniería. Universidad del Zulia, 47(1), p. e244707. doi: 10.22209/rt.v47a07.
Issue
Section
Artículos de Investigación
Copyright (c) 2024 Joel Bayle Yong, Giovany Alemán Carmenate, René Antonio Puig Martínez
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
Copyright
La Revista Técnica de la Facultad de Ingeniería declara que los derechos de autor de los trabajos originales publicados, corresponden y son propiedad intelectual de sus autores. Los autores preservan sus derechos de autoría y publicación sin restricciones, según la licencia pública internacional no comercial ShareAlike 4.0
_2.04__.27_p__._m__.__.png)